ASTM A, Martensitic, Normalized and tempered; Quenched and tempered. See the chemical composition and physical properties of ASTM A Grade CA6NM-A, find alternative materials, and connect with suppliers. See the chemical composition and physical properties of ASTM A Grade 4-A, find alternative materials, and connect with suppliers.
|Published (Last):||4 March 2006|
|PDF File Size:||11.5 Mb|
|ePub File Size:||12.57 Mb|
|Price:||Free* [*Free Regsitration Required]|
The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, molybdenum, vanadium, boron, and copper. Other surface discontinuities shall meet the visual acceptance standards specied in the order. Other temperatures may be used upon agreement between the manufacturer and the purchaser, in which case S 8.
Combining values from the two systems may result in non-conformance with the standard. Examination of Weld Preparation S Within the text, the SI units are shown in brackets. Click here to view all the property values for this datasheet as they were originally entered into MatWeb. All castings shall receive the specified heat treatment requirement: It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.
Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. Other higher specied minimum average and single values may be used upon agreement between the manufacturer and the purchaser.
Tensile properties of the steel shall conform to the requirements for tensile strength, yield strength, elongation, reduction of area, hardness, and maximum thickness. MatWeb is intended for personal, non-commercial use.
Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
Unacceptable visual surface discontinuities shall be removed and their removal veried by visual examination of the resultant cavities. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters.
Subscribe to Premium Services Searches: General Conditions for Delivery 3. Repair By Welding 9. Preliminary heat treatment prior to nal heat treatment as well as multiple tempering is permitted. D Double temper with the nal temper at a lower temperature than the intermediate temper.
This specification covers low-alloy steel and martensitic stainless steels in the normalized and tempered, or quenched and tempered conditions, suitable for pressure-containing parts. Please contact us at webmaster matweb. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility.
ASTM A487 Grade 4-A
Charpy Impact Test S8. The intermediate and nal PWHT temperatures shall be the same as the intermediate and nal tempering temperatures, respectively, as the original heat treatment of the castings.
Users should note that hardenability of some of the grades mentioned may restrict the maximum size at which the required mechanical properties are obtained. Magnetic Particle Inspection S5. Combining values a48 the two systems may result in nonconformance with the specication. Preliminary heat treatment and multiple tempering are permitted. Re—examination of the weld repair by radiography when Supplementary Requirement S 5 has been specied will not be necessary when an applicable surface inspection method was used to locate the discontinuity except for the following: Questions or comments about MatWeb?
We appreciate your input. Property Data This page displays only the text of a material data sheet. Martensitic, Normalized and tempered; Quenched and tempered Key Words: Login to see your most recently viewed materials here. This abstract is a brief summary of the referenced asym.
The contents, results, and technical data from this site may not be reproduced either electronically, photographically or substantively without permission from MatWeb, LLC.
ASTM A / AM – 14e1 Standard Specification for Steel Castings Suitable for Pressure Service
Link to Active This link will always route to the current Active version of the standard. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete asgm up to date.
The weldability of the classes in this specication varies from readily weldable to weldable only with adequate precautions, asm the weldability of each class should be considered prior to assembly by fusion welding.
Originally published as A — 63T. Product analysis tolerance is specified.
ASTM A487 Grade CA6NM-A
A superscript epsilon e indicates an editorial change since the last revision or reapproval. Recording-type pyrometers shall be used to control the furnace temperature.
Product analysis tolerances for stainless grades are not presently applicable pending development of these limits.